EKSTRAKSI TIO2 DARI PASIR BESI MENGGUNAKAN

EKSTRAKSI TIO2 DARI PASIR BESI MENGGUNAKAN METODE PRE-OKSIDASI
DAN LEACHING ASAM KLORIDA
Oleh:
ALMAUN
F1C1 13 044
INTISARI
Telah dilakukan penelitian mengenai ekstraksi TiO2 dari pasir besi menggunakan
metode pre-oksidasi dan leaching asam klorida. Penelitian ini bertujuan untuk mengetahui
pengaruh ekstraksi TiO2 terhadap hasil penggabungan metode pre-oksidasi dan leaching asam
klorida, dan menghasilkan TiO2 dengan kadar tinggi menggunakan metode penggabungan preoksidasi dan leaching asam klorida. Karakterisasi dilakukan menggunakan X-ray flourecence
dan X-ray diffractometer. Analisis menggunakan XRD menunjukkan fasa TiO2 anatase (2
melalui metode pre-oksidasi muncul pada dan 5sedangkan untuk metode nonoksidasi fasa TiO2 rutile (2 muncul 27,65o, dan 62,18o. Analisis bijih ilmenite
teroksidasi menggunakan XRF mampu menghasilkan kadar TiO2 sebesar 91,11 % dan
eliminasi besi oksida sebesar 63,479 % dibandingkan dengan bijih ilmenite non-oksidasi hanya
menghasilkan kadar TiO2 sebanyak 55,27 % dan eliminasi besi oksida sebesar 36,96 %.
Kata kunci : TiO2, Pre-oksidasi, Leaching asam klorida, ilmenite, Besi Oksida.
EXTRACTION OF TIO2 FROM IRON SAND BY USING PRE-OXIDATION AND
CHLORIDE ACID LEACHING METHOD
By:
ALMAUN
F1C1 13 044
ABSTRACT
The study of extraction of TiO2 from iron sand by using pre-oxidation and chloride acid
leaching method has been done. The aims of this study are to know TiO2 extract on the
influence of combination method between pre-oxidation and chloride acid leaching and
chrolride acid leaching and producing of high lecel TiO2 using pre-oxidation and chloride acid
leaching. The characterization were performed using -ray flourecence (XRF) dan X-ray
diffractometer (XRD). XRD analysis showed that the presence of anatase phase (2 of TiO2
using pre-oxidation method atand 5 and rutile phase (2 of TiO2 using chlroride
acid leaching at 27,65o, and 62,18o . XRF analysis of ilminite oxidation produce of TiO2
content of 91,11% and reduce of ferro oxide of 63.479% although non-oxidation of ilminte
producing of TiO2 content of 55,27% and reduce ferro oxide of 36.96%.
Keywords : TiO2, Pre-oxidation, Chloride Acid Leaching, Ilmenite, feroo oxide