Perubahan Honogenitas Struktur Dan Laju Korosi Hasil

Perubahan Homogenitas Struktur Dan Laju Korosi
Hasil Lasan Dissimilar Metal Akibat Penambahan Medan Magnet
(Change Of Structure Homogenety And Corrosion Rate On Dissimilar Metal
Weldment Caused By Magnetic Field Addition)
Sugiarto, Eko Siswanto, Jamasri, Wazis Wildan
Fakultas Teknik Universitas Brawijaya Malang
Abstrak
Struktur yang tidak homogen, cacat las dan kegagalam mekanik menjadi permasalahan yang serius pada
sambungan dissimilar metal,yang umumnya disebabkan efek sirkulasi pada kolam las akibat gaya aktivasi
seperti buoyancy force, marangoni force dan gaya elektromagnetik yang timbul selama pencairan logam. Laju
sirkulasi logam cair dapat ditingkatkan dengan memperbesar gaya aktivasi tersebut. Penambahan medan
magnet eksternal bertujuan untuk memperbesar gaya elektromagnetik yang bekerja pada logam cair agar laju
sirkulasinya meningkat, sehingga struktur sambungan las semakin homogen dan laju korosinya semakin turun.
Penelitian ini menggunakan plat baja ST37 dan plat baja tahan karat (SUS 430) tebal 4 mm yang dilas tumpul
dengan las TIG polaritas balik menggunakan tegangan 30 Volt dan arus 120 Ampere serta pelindung gas argon.
Elektode AWS ER 309 L diameter 2,4 mm digunakan dengan kecepatan las rata-rata 5,8 mm/menit. Kuat
medan magnet eksternal ditambahkan dengan mengalirkan arus DC pada lilitan kawat tembaga diameter 0,4
mm sebanyak 100 lilitan sebesar (3, 5, 10, 12 dan 15 Ampere). Pola pembangkitan medan magnet juga
divariasikan dengan 4 model (pola). Hasilnya adalah, penambahan medan magnet eksternal dalam berbagai
pola menghasilkan penetrasi yang lebih dalam dan homogenitas yang lebih tinggi dibandingkan dengan
pengelasan tanpa penambahan medan magnet. Penambahan medan magnet eksternal dalam berbagai pola
juga efektif dalam menurunkan laju korosi. Korosi cenderung menyerang HAZ dan daerah fusion boundary
akibat adanya daerah unmixed. .
Kata kunci : dissimilar metal, weld pool, medan magnet eksternal, homogenitas struktur dan laju korosi
Change Of Structure Homogenety And Corrosion Rate On Dissimilar Metal Weldment Caused By
Magnetic Field Addition
Abstract
Change of structure homogenety and corrosion rate on dissimilar metal weldment caused by magnetic
field addition. The seriously problem of welding in dissimilar metal are unhomogeneous structure, welding
defect and mechanical failure. It is caused by circulation effect in weld pool on welding process. The circulation
effect is caused by activation force in metal liquefaction such as buoyancy, marangoni and electromagnetic
forces. Circulation rate of liquid metal can be increased by enlargement activation force. The aim of external
magnetic field addition is to enhance electromagnetic force on weld pool in order to increase the circulation
rate. So then, weldment structure become more homogen, whereas the corrotion rate become decrease. The
research is purposed to enlarge activation force by adding external solenoid magnet. Steel plate of ST 37 and
SUS 430 have 4 mm thickness are butt joint welded by reverse polarization of TIG welding that used 30 Volt,
120 A and gas Argon cover. Average of welding speed is 5.8 mm/minute and used AWS ER 309 L electrode has
2.4 mm diameter. Variations of DC current to generate magnetic field in 0.4 mm diameter of Copper with 100
spools are 3, 5, 10, 12 and 15 Ampere.
187
Pattern of magnetic field generation varied in 4 models. The result of research showed that the addition of
magnetic field in all pattern have caused penetration deeply and homogenous structure that higher than
welding without magnetic field. The external magnetic in all pattern effectively decrease corrosion rate. The
tendency of corrosion attacked in HAZ and fusion boundary that caused by unmixed zone.
Keyword : dissimilar metal, weld pool, external magnetic field, homogeneous structure and corrosion rate.